Metal heterocyclic compounds for deposition of thin films

ABSTRACT

Methods and compositions for depositing a metal containing film on a substrate are disclosed. A reactor and at least one substrate disposed in the reactor are provided. A metal containing precursor is provided and introduced into the reactor, which is maintained at a temperature of at least 100° C. A metal is deposited on to the substrate through a deposition process to form a thin film on the substrate.

CROSS-REFERENCE TO RELATED APPLICATIONS

The present application claims the benefit of U.S. Provisional Application Ser. No. 61/075,664, filed Jun. 25, 2008, herein incorporated by reference in its entirety for all purposes.

BACKGROUND

1. Field of the Invention

This invention relates generally to compositions, methods and apparatus for use in the manufacture of semiconductor, photovoltaic, LCF-TFT, or flat panel type devices. More specifically, the invention relates to methods of forming a thing film on a substrate.

2. Background of the Invention

One reason the requirements for suitable metallorganic precursors, used in chemical vapor depositions (CVD) and/or atomic layer depositions (ALD) for semiconductor manufacturing processes, are increasing is due to the high surface coverage required by the deposited films, as compared to that found through physical vapor deposition methods (e.g. PVD, sputtering method).

For example, preferred production methods for GeSbTe alloy thin films, which are used in phase change memory devices, are changing from PVD methods to CVD/ALD methods with the increasing the capacity of memory cell. The demonstration sample of 512 Mega-bit PRAM was made by PVD method under 90 nm technology node processes in 2007, however in the future CVD/ALD methods will likely be necessary for the production of giga-bit scale (and greater) PRAM devices. A main issue for these future production methods is identifying suitable precursors which will allow for a low temperature, low impurity CVD/ALD film deposition. Similar situations are seen in many stages of semiconductor device manufacture. For instance, precursors for deposition of metallic titanium films are needed, due to the high level of impurities observed in the current processes.

Consequently, there exists a need for a need for materials and methods to deposit precursors to form thin films in semiconductor manufacturing processes.

BRIEF SUMMARY

The invention provides novel methods and compositions for the deposition of metal containing films on a substrate. In an embodiment, a method for depositing a metal film on a substrate comprises providing a reactor, and at least one substrate disposed in the reactor. A metal precursor is provided, where the metal precursor is metal-heterocyclic precursor with one of the following general formulas: M(NR(CRR)_(n)NR)_(x)(R)_(y)  (I) M(NRCR═CRNR)_(x)(R)_(y),  (II) M′U_(a)Z_(b)  (III) wherein each R is independently selected from among: H; linear, branched or cyclic C1-C6 alkyls; linear, branched or cyclic C1-C6 alkoxyls; linear, branched or cyclic C1-C6 alkylsilyls; linear, branched or cyclic C1-C6 perfluorocarbons; dialkylaminos of the general formula NR′R″ (wherein R′ and R″ are independently selected from H, C1-C6 alkyls, C1-C6 alkylsilyls, C1-C6 perfluorocarbons, and C1-C6 alkylaminos); C1-C6 alkylimidos or alkylsilyliminos; cyanos; carbonyls; phenyls; benzyls; pyridyls; halogens (such as F, Cl, Br, and I); sulfos; nitros; carboxys; hydroxyls; diazos; and azidos; in the case where R is not substituting part of the cyclometal group, R can be further independently selected from among: an amidinate of the general formula R¹NC(CH3)NR¹; a formamidinate of the general formula R¹NCHNR¹; a β-diketonate of the general formula OCR¹CR¹CR¹O; a β-enaminoketonate of the general formula NR¹CR¹CR¹CR¹O; and a β-diketiminate of the general formula NR¹CR¹CR¹CR¹NR¹; wherein each R¹ is independently selected from among: H; C1-C6 alkyls; C1-C6 alkylsilyls; C1-C6 perfluorocarbons; C1-C6 alkylaminos; dienyls (such as cyclopentadienyl, pentadienyl, cyclohexadienyl, hexadienyl), each dienyl ligand being substituted or not by C1-C6 linear or branched alkyl groups or C1-C6 linear or branched alkoxy groups; dienes (such as cyclohexadiene, hexadiene, norbornadiene, butadiene, cyclopentadiene, pentadiene, cyclooctadiene), each diene ligand being substituted or not by C1-C6 linear or branched alkyl groups or C1-C6 linear or branched alkoxy groups; M is at least one member selected from the group consisting of: Be; B; Mg; Al; Si; P; S; Ca; Sc; Ti; V; Cr; Mn; Fe; Co; Ni; Cu; Zn; Ga; Ge; As; Se; Sr; Y; Zr; Nb; Mo; Ru; Rh; Pd; Ag; Cd; In; Sn; Sb; Te; Ba; La; Ce; Pr; Nd; Sm; Eu; Gd; Tb; Dy; Ho; Er; Tm; Yb; Lu; Hf; Ta; W; Re; Os; Ir; Pt; Au; Hg; Tl; Pb; and Bi; M′ is at least one member selected from the group consisting of: Be; B; C; Mg; Al; Si; P; S; Ca; Sc; Ti; V; Cr; Mn; Fe; Co; Ni; Cu; Zn; Ga; Ge; As; Se; Sr; Y; Zr; Nb; Mo; Ru; Rh; Pd; Ag; Cd; In; Sn; Sb; Te; Ba; La; Ce; Pr; Nd; Sm; Eu; Gd; Tb; Dy; Ho; Er; Tm; Yb; Lu; Hf; Ta; W; Re; Os; Ir; Pt; Au; Hg; Tl; Pb; and Bi; each U is independently selected from among: H; C1-C6 alkyls; C1-C6 alkylsilyls; C1-C6 perfluorocarbons; dialkylaminos of the general formula NR′R″ (wherein R′ and R″ are independently selected from H, C1-C6 alkyls, C1-C6 alkylsilyls, C1-C6 perfluorocarbons, and C1-C6 alkylaminos); cyanos; carbonyls; phenyls; benzyls; pyridyls; halogens (such as F, Cl, Br, and I); sulfos; nitros; carboxys; hydroxyls; diazos; azidos; amidinates of the general formula R¹NC(CH3)NR¹; formamidinates of the general formula R¹NCHNR¹; β-diketonates of the general formula OCR¹CR¹CR¹O; β-enaminoketonates of the general formula NR¹CR¹CR¹CR¹O; and β-diketiminates of the general formula NR¹CR¹CR¹CR¹NR¹; wherein each R¹ is independently selected from among: H; C1-C6 alkyls; C1-C6 alkylsilyls; C1-C6 perfluorocarbons; C1-C6 alkylaminos; dienyls (such as cyclopentadienyl, pentadienyl, cyclohexadienyl, hexadienyl), each dienyl ligand being substituted or not by C1-C6 linear or branched alkyl groups or C1-C6 linear or branched alkoxy groups; each Z is independently selected from the metal-heterocyclic precursors of general formula (I) or (II), wherein the oxidation state of the metal-heterocyclic precursor of general formula (I) or (II) has an oxidation state which allows for a coordination between M and M′; n is an integer such that 1≦n≦5; x and y are integers independently determined based upon the oxidation state of M, such that x+y=oxidation state of M; and a and by are integers independently determined based upon the oxidation state of M′, such that a+b=oxidation state of M.

Other embodiments of the current invention may include, without limitation, one or more of the following features:

-   -   the metal precursor contains an imido bond, the total number of         R groups in the metal precursor is greater than or equal to two,         and two R groups are substituted by one imido ligand;     -   the metal precursor is of general formula (III) and in the Z         portion of the molecule, at least one R group which is indexed         by the y variable is substituted with a direct M to M′ bond;     -   maintaining the reactor at a temperature between about 100° C.         and about 500° C., and preferably between about 200° C. and         about 350° C.;     -   maintaining the reactor at a pressure between about 1 Pa and         about 10⁵ Pa, and preferably between about 25 Pa and about 10³         Pa;     -   introducing at least one reducing gas into the reactor, wherein         the reducing gas is at least one of: hydrogen; ammonia; silane;         disilane; trisilane; hydrogen radicals; and mixtures thereof;     -   introducing at least one oxidizing gas into the reactor, wherein         the oxidizing gas is at least one of: oxygen; ozone; water;         hydrogen peroxide; nitric oxide; nitrous oxide; oxygen radicals;         and mixtures thereof;     -   the metal precursor and the reducing gas and/or the oxidizing         gas are introduced into the chamber either substantially         simultaneously or sequentially;     -   the metal precursor and the reducing gas and/or the oxidizing         gas are introduced into the chamber substantially simultaneously         and the chamber is configured for chemical vapor deposition;     -   the metal precursor and the reducing gas and/or oxidizing gas         are introduced into the chamber sequentially and the chamber is         configured for atomic layer deposition;     -   the deposition process is a plasma enhanced deposition process         (ALD or CVD); and     -   a metal containing thin film coated substrate.

The foregoing has outlined rather broadly the features and technical advantages of the present invention in order that the detailed description of the invention that follows may be better understood. Additional features and advantages of the invention will be described hereinafter that form the subject of the claims of the invention. It should be appreciated by those skilled in the art that the conception and the specific embodiments disclosed may be readily utilized as a basis for modifying or designing other structures for carrying out the same purposes of the present invention. It should also be realized by those skilled in the art that such equivalent constructions do not depart from the spirit and scope of the invention as set forth in the appended claims.

Notation and Nomenclature

Certain terms are used throughout the following description and claims to refer to various components and constituents. This document does not intend to distinguish between components that differ in name but not function.

As used herein, the term “alkyl group” refers to saturated functional groups containing exclusively carbon and hydrogen atoms. Further, the term “alkyl group” may refer to linear, branched, or cyclic alkyl groups. Examples of linear alkyl groups include without limitation, methyl groups, ethyl groups, propyl groups, butyl groups, etc. Examples of branched alkyls groups include without limitation, t-butyl. Examples of cyclic alkyl groups include without limitation, cyclopropyl groups, cyclopentyl groups, cyclohexyl groups, etc.

As used herein, the abbreviation, “Me,” refers to a methyl group; the abbreviation, “Et,” refers to an ethyl group; the abbreviation, “t-Bu,” refers to a tertiary butyl group; the abbreviation “iPr”, refers to an isopropyl group; the abbreviation “acac”, refers to acetylacetonato; and the abbreviation “Cp” refers to a cyclopentadienyl group.

As used herein the abbreviations: Be; B; C; N; Mg; Al; Si; P; S; Ca; Sc; Ti; V; Cr; Mn; Fe; Co; Ni; Cu; Zn; Ga; Ge; As; Se; Sr; Y; Zr; Nb; Mo; Ru; Rh; Pd; Ag; Cd; In; Sn; Sb; Te; Ba; La; Ce; Pr; Nd; Sm; Eu; Gd; Tb; Dy; Ho; Er; Tm; Yb; Lu; Hf; Ta; W; Re; Os; Ir; Pt; Au; Hg; Tl; Pb; and Bi generally refer to the corresponding elements from the periodic table of elements.

As used herein, the term “independently” when used in the context of describing R groups should be understood to denote that the subject R group is not only independently selected relative to other R groups bearing different subscripts or superscripts, but is also independently selected relative to any additional species of that same R group. For example in the formula MR¹ _(x) (NR²R³)_((4-x)), where x is 2 or 3, the two or three R¹ groups may, but need not be identical to each other or to R² or to R³. Further, it should be understood that unless specifically stated otherwise, values of R groups are independent of each other when used in different formulas.

BRIEF DESCRIPTION OF THE DRAWINGS

For a further understanding of the nature and objects for the present invention, reference should be made to the following detailed description, taken in conjunction with the accompanying drawings, in which like elements are given the same or analogous reference numbers and wherein:

FIG. 1 illustrates schematic representations of chemical structures corresponding to the metal precursor, as according to various embodiments of the current invention.

DESCRIPTION OF PREFERRED EMBODIMENTS

Generally, embodiments of the current invention relate to methods and compositions for the deposition of a metal containing film on a substrate through the use of a metal precursor. Generally, and as described above, the metal precursor is a metal-heterocyclic precursor with one of the following general formulas: M(NR(CRR)_(n)NR)_(x)(R)_(y)  (I) M(NRCR═CRNR)_(x)(R)_(y),  (II) M′U_(a)Z_(b)  (III)

In embodiments where the metal precursor has the general formula (I), the precursor may be shown structurally as in: FIG. 1( a) where an embodiment of the general formula (I) as M(RNCRRCRRNR)— is shown; FIG. 1( c) an embodiment of the general formula (I) as M(NRCRRCRRRNR)(NRCRCRRNR) is shown; FIG. 1( d) where an embodiment of the general formula (I) as M(NRCRRCRRNR)(NRCRRCRRNR)(NRCRRCRRNR) is shown; FIG. 1( e) where an embodiment the general formula (i) as M(NRCRRCRRNR)R is shown; FIG. 1( g) where an embodiment of the general formula (I) as M(NRCRRCRRNR)RR is shown; FIG. 1( i) where an embodiment of the general formula (I) as M(NRCRRCRRNR)RRR is shown; FIG. 1( k) where an embodiment of the general formula (I) as (NRCRRCRRNR)M(NRCRRCRRNR)—RR is shown; FIG. 1( l) where an embodiment of the general formula (I) as M(NRCRRCRRCRRNR) is shown; and FIG. 1( m) where an embodiment of the general formula (I) as (NRCRRCRRCRRNR)M(NRCRRCRRCRRNR) is shown.

Examples of the precursors covered by general formula (I) include, but are not limited to: Ge(CH₃NCH₂CH₂NCH₃); Ge(C₂H₅NCH₂CH₂NC₂H₅); Ge(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Ge(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Te(CH₃NCH₂CH₂NCH₃); Te(C₂H₅NCH₂CH₂NC₂H₅); Te(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Te(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Te(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Ti(CH₃NCH₂CH₂NCH₃); Ti(C₂H₅NCH₂CH₂NC₂H₅); Ti(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Ti(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Si(CH₃NCH₂CH₂NCH₃); Si(C₂H₅NCH₂CH₂NC₂H₅); Si(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Si(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Sn(CH₃NCH₂CH₂NCH₃); Sn(C₂H₅NCH₂CH₂NC₂H₅); Sn(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Sn(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Te(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Fe(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)₃; Ru(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)₃; Sb(N(CH₃)CH₂CH₂N(CH₃))(NMe₂); Sb(N(CH₃)CH₂CH₂N(CH₃))(CH₃); Sb(N(CH₃)CH₂CH₂N(CH₃))(C₂H₅); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(CH₃); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(C₂H₅); Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Hf(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Zr(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Ti(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Si(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Ge(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Hf(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Zr(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Ti(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Si(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Ge(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Hf(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Zr(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Ru(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Fe(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Os(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Ta(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂)₃; Nb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂)₃; Nb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(CH₃)₃; Nb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(C₂H₅)₃; Os(N(C(CH₃)₃CH₂CH₂N(C(CH₃)₃)₂(C₅H₅); Fe(N(C(CH₃)₃CH₂CH₂N(C(CH₃)₃)₂(C₅H₅); Ru(N(C(CH₃)₃CH₂CH₂N(C(CH₃)₃)₂(C₅H₅); Ge(N(CH₃)CH₂CH₂CH₂N(CH₃)); Ge(NC(CH₃)₃CH₂CH₂CH₂N(CH₃)₃); Ti(N(CH₃)CH₂CH₂CH₂N(CH₃)); Ti(NC(CH₃)₃CH₂CH₂CH₂N(CH₃)₃); Si(N(CH₃)CH₂CH₂CH₂N(CH₃)); Si(NC(CH₃)₃CH₂CH₂CH₂N(CH₃)₃); Ge(N(CH₃)CH₂CH₂CH₂N(CH₃))₂; Ge(N(C₂H₅)CH₂CH₂CH₂N(C₂H₅))₂; Ti(N(CH₃)CH₂CH₂CH₂N(CH₃))₂; Ti(N(C₂H₅)CH₂CH₂CH₂N(C₂H₅))₂; Si(N(CH₃)CH₂CH₂CH₂N(CH₃))₂; and Si(N(C₂H₅)CH₂CH₂CH₂N(C₂H₅))₂.

In embodiments where the metal precursor has the general formula (II), the precursor may be shown structurally as in: FIG. 1( b) where an embodiment of the general formula (II) as M(RNCRCRNR) is shown; FIG. 1( f) where an embodiment of general formula (II) as M(NRCR═CRNR)R is shown; FIG. 1( h) where an embodiment of general formula (II) as M(NRCR═CRNR)RR is shown; and FIG. 1( j) where an embodiment of the general formula (II) as M(NRCR═CRNR)RRR is shown.

Examples of the precursors covered by general formula (II) include, but are not limited to: Ge(NCH₃CHCHNCH₃); Ge(C₂H₅NCHCHNC₂H₅); Ge(NCH(CH₃)₂CHCHNCH(CH₃)₂); Ge(NC(CH₃)₃CHCHNC(CH₃)₃); Ge(NC(CH₃)₃NC(CH₃)C(CH₃)NC(CH₃)₃); Te(CH₃NCHCHNCH₃); Te(C₂H₅NCHCHNC₂H₅); Te(NCH(CH₃)₂CHCHNCH(CH₃)₂); Te(NC(CH₃)₃CHCHNC(CH₃)₃); Te(NC(CH₃)₃C(CH₃)C(CH₃)NC(CH₃)₃); Ti(CH₃NCHCHNCH₃); Ti(C₂H₅NCHCHNC₂H₅); Ti(NCH(CH₃)₂CHCHNCH(CH₃)₂); Ti(NC(CH₃)₃NCHCHNC(CH₃)₃); Ti(NC(CH₃)₃NC(CH₃)C(CH₃)NC(CH₃)₃); Si(CH₃NCHCHNCH₃); Si(C₂H₅NCHCHNC₂H₅); Si(NCH(CH₃)₂CHCHNCH(CH₃)₂); Si(NC(CH₃)₃CHCHNC(CH₃)₃); Si(NC(CH₃)₃NC(CH₃)C(CH₃)NC(CH₃)₃); Sn(NCH₃NCHCHNCH₃); Sn(C₂H₅NCHCHNC₂H₅); Sn(NCH(CH₃)₂CHCHNCH(CH₃)₂); Sn(NC(CH₃)₃CHCHNC(CH₃)₃); Sn(NC(CH₃)₃C(CH₃)C(CH₃)NC(CH₃)₃); Sb(N(CH₃)CHCHN(CH₃))(N(CH₃)₂); Sb(N(CH₃)CHCHN(CH₃))(CH₃); Sb(N(CH₃)CHCHN(CH₃))(C₂H₅); Sb(NC(CH₃)₃CHCHNC(CH₃)₃)(N(CH₃)₂); Sb(NC(CH₃)₃CHCHNC(CH₃)₃)(CH₃); Sb(NC(CH₃)₃CHCHNC(CH₃)₃)(C₂H₅); Ru(NC(CH₃)₃CHCHNC(CH₃)₃)(C₅H₅); Ti(NC(CH₃)₃CHCHNC(CH₃)₃)(N(CH₃)₂)₂; Si(NC(CH₃)₃CHCHNC(CH₃)₃)(N(CH₃)₂)₂; Ge(NC(CH₃)₃CHCHNC(CH₃)₃)(N(CH₃)₂)₂; Sn(NC(CH₃)₃CHCHN(C(CH₃)₃)(N(CH₃)₂)₂; Ti(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(CH₃)₂; Si(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(CH₃)₂; Ge(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(CH₃)₂; Ti(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(C₂H₅)₂; Si(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(C₂H₅)₂; Ge(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(N(C₂H₅)₂); Si(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(C₂H₅)₂; Ru(NC(CH₃)₃CHCHN(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Fe(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Os(N(C(CH₃)₃)CHCHN(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Ta(NC(CH₃)₃CHCHNC(CH₃)₃)(NMe₂)₃; Ta(NC(CH₃)₃CHCHNC(CH₃)₃)(CH₃)₃; Ta(NC(CH₃)₃CHCHNC(CH₃)₃)(C₂H₅)₃; Nb(NC(CH₃)₃CHCHNC(CH₃)₃)(NMe₂)₃; Nb(NC(CH₃)₃CHCHNC(CH₃)₃)(CH₃)₃; and Nb(NC(CH₃)₃CHCHNC(CH₃)₃)(C₂H₅)₃.

In some embodiments, the precursor may be of general formula (III), where each Z is independently selected from the precursors of general formula (I) or (II), and where the oxidation state of the selected precursor is such as to allow a coordination between M and M′. This coordination can vary in form depending upon the individual precursors. In some embodiments the coordination may be a bimetallic bond, but in other embodiments the coordination can be a much weaker association, such as in the case of pyridine which could be considered crystalline solvent type coordination.

Examples of the precursors covered by general formula (III) include, but are not limited to: Ni(Si(NC(CH₃)₃C(—CHCHCH—)CNC(CH₃)₃))₄; Ni(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₃; Ni(Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(CO)₃; Ni(Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(CO)₂; Ni(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(CO)₂; Ni(Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₃; Co(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₃; Co(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(CO)₂; Si(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₄; Ti(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₄; Ge(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₄; Sb(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₃; Te(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂; Te(Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂; Te(Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂; Hf(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₄; Zr(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₄; Ti(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(CH₃)₂)₂; Ge(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(CH₃)₂)₂; Te(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(N(CH₃)₂); Te(Ge(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(N(CH₃)₂); Sb(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(N(CH₃)₂)₂; Cr(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(CO)₄; Mo(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(CO)₄; W(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(CO)₄; Cr(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(Cp)₂; Mo(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(Cp)₂; W(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(Cp)₂; Ru(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(CO)₃; Ru(C₅H₅)(CN)(CO)(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)); Ru(C₆H₆)(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(((CH₃)₂CH)NC(CH₃)N(CH(CH₃)₂)); Os(C₅H₅)(CN)(CO)(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)); Os(C₆H₆)(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(((CH₃)₂CH)NC(CH₃)N(CH(CH₃)₂); Fe(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(CO)₄; Fe(C₅H₅)(CN)(CO)(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)); Fe(C₆H₆)(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(((CH₃)₂CH)NC(CH₃)N(CH(CH₃)₂)); Ca(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(NMe₂)₂; Sr(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(NMe₂)₂; Ba(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(NMe₂)₂; Ca(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(SiMe₃)₂)₂; Sr(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(SiMe₃)₂)₂; Ba(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(SiMe₃)₂)₂; Sn(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(NMe₂)₂; Sn(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂Cl₂; Sm(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(C₅H₅)₂; Sm(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(C₅H₅)₂; Yb(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(C₅H₅)₂; Yb(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(C₅H₅)₂; Eu(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(acac)₃; Eu(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(acac)₃; Y(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(acac)₃; Y(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(acac)₃; La(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(N(Si(CH₃)₃)₃; La(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(N(Si(CH₃)₃)₃; Y(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(N(Si(CH₃)₃)₃, Y(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(N(Si(CH₃)₃)₃; La(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(Si(H₂Me))₂)₃; La(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(Si(H₂Me))₂)₃; Y(C(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(Si(H₂Me))₂)₃; Y(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))₂(N(Si(H₂Me))₂)₃; Rh(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(C₈H₁₂)(((CH₃)₂CH)NC(CH₃)N (CH(CH₃)₂)); Ta(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(NMe₂)₄; Mg(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(Et)₂; Zn(Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))(Et)₂; (Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))AlMe₃; (Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))GaMe₃; and (Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃))AlH₃.

Generally, the disclosed precursors may be deposited to form a thin film using any deposition methods known to those of skill in the art. In some embodiments the depositions are through a chemical vapor deposition (CVD) or atomic layer deposition (ALD) method. Examples of suitable deposition methods include without limitation, conventional CVD, low pressure chemical vapor deposition (LPCVD), plasma enhanced chemical vapor depositions (PECVD), atomic layer deposition (ALD), pulsed chemical vapor deposition (P-CVD), plasma enhanced atomic layer deposition (PE-ALD), or combinations thereof.

In an embodiment, the metal precursor is introduced into a reactor in vapor form. The precursor in vapor form may be produced by vaporizing a liquid precursor solution, through a conventional vaporization step such as direct vaporization, distillation, or by bubbling an inert gas (e.g. N₂, He, Ar, etc.) into the precursor solution and providing the inert gas plus precursor mixture as a precursor vapor solution to the reactor. Bubbling with an inert gas may also remove any dissolved impurities (e.g. oxygen) present in the precursor solution.

The reactor may be any enclosure or chamber within a device in which deposition methods take place such as without limitation, a cold-wall type reactor, a hot-wall type reactor, a single-wafer reactor, a multi-wafer reactor, or other types of deposition systems under conditions suitable to cause the precursors to react and form the layers.

Generally, the reactor contains one or more substrates on to which the thin films will be deposited. The one or more substrates may be any suitable substrate used in semiconductor, photovoltaic, flat panel, or LCD-TFT device manufacturing. Examples of suitable substrates include without limitation, silicon substrates, silica substrates, silicon nitride substrates, silicon oxy nitride substrates, tungsten substrates, or combinations thereof. Additionally, substrates comprising tungsten or noble metals (e.g. platinum, palladium, rhodium, or gold) may be used. The substrate may also have one or more layers of differing materials already deposited upon it from a previous manufacturing step.

In some embodiments, in addition to the metal precursor, a reactant gas may also be introduced into the reactor. In some of these embodiments, the reactant gas may be an oxidizing gas such as one of oxygen, ozone, water, hydrogen peroxide, nitric oxide, nitrogen dioxide, radical species of these, as well as mixtures of any two or more of these. In some other of these embodiments, the reactant gas may be a reducing gas such as one of hydrogen, ammonia, a silane (e.g. SiH₄; Si₂H₆, Si₃H₈), SiH₂Me₂; SiH₂Et₂; N(SiH₃)₃; radical species of these, as well as mixtures of any two or more of these.

In some embodiments, and depending on what type of film is desired to be deposited, a second precursor may be introduced into the reactor. The second precursor comprises another metal source, such as copper, praseodymium, manganese, ruthenium, titanium, tantalum, bismuth, zirconium, hafnium, lead, niobium, magnesium, aluminum, lanthanum, or mixtures of these. In embodiments where a second metal containing precursor is utilized, the resultant film deposited on the substrate may contain at least two different metal types.

The metal precursor and any optional reactants or precursors may be introduced sequentially (as in ALD) or simultaneously (as in CVD) into the reaction chamber. In some embodiments, the reaction chamber is purged with an inert gas between the introduction of the precursor and the introduction of the reactant. In one embodiment, the reactant and the precursor may be mixed together to form a reactant/precursor mixture, and then introduced to the reactor in mixture form. In some embodiments, the reactant may be treated by a plasma, in order to decompose the reactant into its radical form. In some of these embodiments, the plasma may generally be at a location removed from the reaction chamber, for instance, in a remotely located plasma system. In other embodiments, the plasma may be generated or present within the reactor itself. One of skill in the art would generally recognize methods and apparatus suitable for such plasma treatment.

In some embodiments, the temperature and the pressure within the reactor are held at conditions suitable for ALD or CVD depositions. For instance, the pressure in the reactor may be held between about 1 Pa and about 10⁵ Pa, or preferably between about 25 Pa and 10³ Pa, as required per the deposition parameters. Likewise, the temperature in the reactor may be held between about 100° C. and about 500° C., preferably between about 200° C. and about 350° C.

Depending on the particular process parameters, deposition may take place for a varying length of time. Generally, deposition may be allowed to continue as long as desired or necessary to produce a film with the necessary properties. Typical film thicknesses may vary from several hundred angstroms to several hundreds of microns, depending on the specific deposition process. The deposition process may also be performed as many times as necessary to obtain the desired film.

In some embodiments, the precursor vapor solution and the reaction gas, may be pulsed sequentially or simultaneously (e.g. pulsed CVD) into the reactor. Each pulse of precursor may last for a time period ranging from about 0.01 seconds to about 10 seconds, alternatively from about 0.3 seconds to about 3 seconds, alternatively from about 0.5 seconds to about 2 seconds. In another embodiment, the reaction gas may also be pulsed into the reactor. In such embodiments, the pulse of each gas may last for a time period ranging from about 0.01 seconds to about 10 seconds, alternatively from about 0.3 seconds to about 3 seconds, alternatively from about 0.5 seconds to about 2 seconds.

EXAMPLES

The following non-limiting examples are provided to further illustrate embodiments of the invention. However, the examples are not intended to be all inclusive and are not intended to limit the scope of the inventions described herein.

Prophetic Example 1

Titanium films may be deposited at temperatures above 200° C. Vapors of the precursor Ti(N(tBu)CH₂CH₂N(tBu))(NMe₂)₂ may be delivered to a reaction furnace using N₂ as a carrier gas, as well as for dilution purposes. Hydrogen may be used as a reactant.

In this way, titanium films are expected to be obtained in ALD mode at temperatures above 200 C.

It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method will be below the detection limit of the apparatus.

Prophetic Example 2

Titanium nitride films are expected to be deposited, as described in Example 1, when ammonia is used instead of hydrogen.

Prophetic Example 3

Germanium films may be deposited at temperatures above 200° C. Vapors of the precursor Ge(N(tBu)CHCHN(tBu))(NMe₂)₂ may be delivered to a reaction furnace using N₂ as a carrier gas, as well as for dilution purposes. Hydrogen may be used as a reactant.

In this way, germanium films are expected to be obtained in ALD mode at temperatures above 200 C.

It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method, will be below the detection limit of the apparatus.

Prophetic Example 4

Germanium nitride films are expected to be deposited, as described in Example 3, when ammonia is used instead of hydrogen.

Prophetic Example 5

Zirconium oxide films may be deposited at temperatures above 220° C. Vapors of the precursor Zr(N(tBu)CH₂CH₂N(tBu))(NMe₂)₂ may be delivered to a reaction furnace using N₂ as a carrier gas, as well as for dilution purposes. Water may be used as a reactant.

In this way, zirconium oxide films are expected to be obtained in ALD mode at temperatures above 200 C.

It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method, will be below the detection limit of the apparatus.

Prophetic Example 6

Zirconium oxide films are expected to be deposited, as described in Example 5, when ozone is used instead of water.

Prophetic Example 7

Nickel films may be deposited at temperatures above 200° C. Vapors of the precursor Ni(SiNC(CH₃)₃CH₂CH₂NC(CH₃)₃)₄ may be delivered to a reaction furnace using N₂ as a carrier gas, as well as for dilution purposes. Hydrogen may be used as a reactant.

In this way, nickel films are expected to be obtained in ALD mode at temperatures above 200 C.

It is expected that the concentrations of various undesired elements in the deposited metal films when analyzed by an Auger spectrometry method, will be below the detection limit of the apparatus.

While embodiments of this invention have been shown and described, modifications thereof can be made by one skilled in the art without departing from the spirit or teaching of this invention. The embodiments described herein are exemplary only and not limiting. Many variations and modifications of the composition and method are possible and within the scope of the invention. Accordingly the scope of protection is not limited to the embodiments described herein, but is only limited by the claims which follow, the scope of which shall include all equivalents of the subject matter of the claims. 

What is claimed is:
 1. A method of forming a metal containing film on a substrate, comprising: a) providing a reactor and at least one substrate disposed therein; b) introducing a metal precursor into the reactor, wherein the metal precursor is selected from the group consisting of: Te(CH₃NCH₂CH₂NCH₃); Te(C₂H₅NCH₂CH₂NC₂H₅); Te(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Te(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Te(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Ti(CH₃NCH₂CH₂NCH₃); Ti(C₂H₅NCH₂CH₂NC₂H₅); Ti(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Ti(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Si(CH₃NCH₂CH₂NCH₃); Si(C₂H₅NCH₂CH₂NC₂H₅); Si(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Si(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Sn(CH₃NCH₂CH₂NCH₃); Sn(C₂H₅NCH₂CH₂NC₂H₅); Sn(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Sn(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Te(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); (NC(CH₃)₃CH₂CH₂NC(CH₃)₃)Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Fe(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)₃; Ru(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)₃; Sb(N(CH₃)CH₂CH₂N(CH₃))(NMe₂); Sb(N(CH₃)CH₂CH₂N(CH₃))(CH₃); Sb(N(CH₃)CH₂CH₂N(CH₃))(C₂H₅); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(CH₃); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(C₂H₅); Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Hf(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Zr(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Ni(SiNC(CH₃)₃CH₂CH₂NC(CH₃)₃)₄, Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Ti(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Si(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Hf(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Zr(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(CH₃)₂; Ti(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Si(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Hf(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Zr(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(C₂H₅)₂; Ru(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Fe(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Os(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Ta(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂)₃; Nb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂)₃; Nb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(CH₃)₃; Nb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(C₂H₅)₃; Os(N(C(CH₃)₃CH₂CH₂N(C(CH₃)₃)₂(C₅H₅); Fe(N(C(CH₃)₃CH₂CH₂N(C(CH₃)₃)₂(C₅H₅); Ru(N(C(CH₃)₃CH₂CH₂N(C(CH₃)₃)₂(C₅H₅); Ti(N(CH₃)CH₂CH₂CH₂N(CH₃)); Ti(NC(CH₃)₃CH₂CH₂CH₂N(CH₃)₃); Si(N(CH₃)CH₂CH₂CH₂N(CH₃)); Si(NC(CH₃)₃CH₂CH₂CH₂N(CH₃)₃); Ti(N(CH₃)CH₂CH₂CH₂N(CH₃))₂; Ti(N(C₂H₅)CH₂CH₂CH₂N(C₂H₅))₂; Si(N(CH₃)CH₂CH₂CH₂N(CH₃))₂; and Si(N(C₂H₅)CH₂CH₂CH₂N(C₂H₅))₂; c) maintaining the reactor at a temperature of at least about 100° C.; and d) decomposing the metal precursor onto the substrate to form a metal containing film.
 2. The method of claim 1, wherein the precursor comprises at least one member selected from the group consisting of: Te(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Te(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Te(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Ti(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Ti(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Si(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Si(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Sn(NCH(CH₃)₂CH₂CH₂NCH(CH₃)₂); Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃); Sn(NCH(CH₃)₂C(CH₃)HC(CH₃)HNCH(CH₃)₂); Ru(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)₃; Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(CH₃); Sb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(C₂H₅); Ti(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Si(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Hf(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Zr(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Sn(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(N(CH₃)₂)₂; Ru(N(C(CH₃)₃)CH₂CH₂N(C(CH₃)₃)(iPrNC(CH₃)NiPr)₂; Ta(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂)₃; and Nb(NC(CH₃)₃CH₂CH₂NC(CH₃)₃)(NMe₂)₃.
 3. The method of claim 1, wherein the precursor comprises at least one member selected from the group consisting of: Ti(N(tBu)CH₂CH₂N(tBu))(NMe₂)₂; Zr(N(tBu)CH₂CH₂N(tBu))(NMe₂)₂; and Ni(SiNC(CH₃)₃CH₂CH₂NC(CH₃)₃)₄.
 4. The method of claim 1, further comprising maintaining the reactor at a temperature between about 100° C. to about 500° C.
 5. The method of claim 4, further comprising maintaining the reactor at a temperature between about 200° C. and about 350° C.
 6. The method of claim 1, further comprising maintaining the reactor at a pressure between about 1 Pa and about 10⁵ Pa.
 7. The method of claim 6, further comprising maintaining the reactor at a pressure between about 25 Pa and about 10³ Pa.
 8. The method of claim 1, further comprising introducing at least one reducing gas into the reactor, wherein the reducing gas comprises at least one member selected from the group consisting of: H₂; NH₃, SiH₄; Si₂H₆; Si₃H₈; hydrogen radicals; and mixtures thereof.
 9. The method of claim 8, wherein the metal precursor and the reducing gas are introduced into the chamber either substantially simultaneously, or sequentially.
 10. The method of claim 9, wherein the reducing gas and the metal precursor are introduced into the chamber substantially simultaneously, and the chamber is configured for chemical vapor deposition.
 11. The method of claim 9, the reducing gas, and the metal precursor are introduced into the chamber sequentially, and the chamber is configured for atomic layer deposition.
 12. The method of claim 1, further comprising introducing at least one oxidizing gas into the reactor, wherein the oxidizing gas comprises at least one member selected from the group consisting of: O₂; O₃; H₂O; H₂O₂; NO; N₂O, oxygen radicals; and mixtures thereof.
 13. The method of claim 12, wherein the metal containing precursor and the oxidizing gas are introduced into the chamber either substantially simultaneously, or sequentially.
 14. The method of claim 12, wherein the metal containing precursor and the oxidizing gas are introduced into the chamber substantially simultaneously, and the chamber is configured for chemical vapor deposition.
 15. The method of claim 12, wherein the metal containing precursor and the oxidizing gas are introduced into the chamber sequentially, and the chamber is configured for atomic layer deposition.
 16. The method of claim 1, wherein the precursor is Zr(N(tBu)CH₂CH₂N(tBu))(NMe₂)₂. 